| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔体流动速率 | 125℃/2.16kg | ASTM D-1238 | 65 | g/10min |
| 熔体流动速率 | 125℃/2.16kg | ISO 1133 | 65 | g/10min | |
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 1300 | g/10min | |
| 熔体流动速率 | 190℃/2.16kg | ISO 1133 | 1300 | g/10min | |
| 单体含量 | Internal Method | 20 | % | ||
| 物理性能 | 比重 | ASTM D-792 | 0.955 | g/cm3 | |
| 比重 | ISO 1183 | 0.955 | g/cm3 | ||
| 机械性能 | 拉伸模量-2% Secant | Compression Molded | ASTM D-638 | 22.1 | MPa |
| 拉伸模量-2% Secant | Compression Molded | ISO 527-2 | 22.1 | MPa | |
| 拉伸断裂强度 | Compression Molded | ASTM D-638 | 6.21 | MPa | |
| 拉伸断裂强度 | Compression Molded | ISO 527-2 | 6.21 | MPa | |
| 拉伸断裂伸长率 | Compression Molded | ASTM D-638 | 350 | % | |
| 拉伸断裂伸长率 | Compression Molded | ISO 527-2 | 350 | % | |
| 热性能 | 维卡软化点 | ASTM D-1525 | 40 | ℃ | |
| 维卡软化点 | ISO 306 | 40 | ℃ | ||
| 熔融温度 | Internal Method | 75 | ℃ | ||